ABSTRACT
Introduction: In an attempt to manage noncavitated carious lesions noninvasively through remineralization, a range of novel fluoride varnishes with additional remineralizing agents have been made available for clinical application. Aim and Objectives: The aim of this study was to compare and evaluate the remineralization potential of three commercially available varnishes on artificial enamel lesions. Materials and Methods: This in vitro study involves eighty intact enamel specimens prepared from premolars extracted for orthodontic purposes. After specimen preparation, the eighty samples were divided randomly into two groups (n = 40) for measurement of baseline surface Vickers microhardness and baseline calcium/phosphorus ratio (% weight) through EDAX testing. Thereafter, the specimens were subjected to demineralization for 96 h to induce initial enamel lesions and the measurements were repeated. Following demineralization, each of the two groups was divided randomly into four subgroups (n = 10) from which one was used as the control group and the others three were allotted to each of the three test varnishes. After varnish application, all the specimens were subjected to a pH cycling regimen that included alternative demineralization (3 h) and remineralization (21 h) daily, for 5 consecutive days. The Vickers microhardness and EDAX measurements were then repeated. Results: One-way ANOVA and post hoc Tukey's tests were conducted for multiple group comparison. All the three commercially available varnishes were capable of remineralizing initial enamel lesions that were induced artificially. No difference was noted in the remineralizing efficacy of the varnishes despite their different compositions. MI Varnish™ (casein phosphopeptide-amorphous calcium phosphate fluoride varnish) showed slightly better recovery in surface microhardness as compared to the other two varnishes. Conclusion: All the varnishes used in this in vitro study are capable of reversing early enamel lesions.
ABSTRACT
Background: Silver diamine fluoride (SDF) is already proven as an antibacterial agent in vitro. Present study was formulated to compare the efficacy of SDF as an antibacterial as well as antiplaque agent in vivo with fluoride varnish and acidulated phosphate fluoride (APF) gel. Study Design: Total 123 children (male = 82, female = 41) were included in the study for a period of 18 months. Children were divided into three different groups-Group 1: SDF; Group 2: fluoride varnish; and Group 3: APF gel. All subjects were evaluated via plaque score at 6 th , 12 th , and 18 th months as well as Streptococcus mutans counts in saliva at 72 h, 6 th , 12 th , and 18 th months of follow-up. Results: Significant reduction was found in plaque score as well as S. mutans counts irrespective of group division. On intergroup comparison, no statistically significant difference was found in plaque score, but significant reduction in S. mutans counts was found in Group 1 as compared with Groups 2 and 3, while no significant difference was found between Groups 2 and 3. Conclusion: In vivo application of SDF on enamel significantly decreases S. mutans counts as compared to fluoride varnish and APF gel.